ARAMID REINFORCEMENTS

Aramid fibres are known for their outstanding stiffness and resistance to high temperature and chemicals. They are used in applications requiring high toughness, crash and abrasion resistance. Aramid fibres are used for plastic reinforcements, ballistic applications such as bulletproof vests or hard ballistic plates. The most common aramid fibre is Kevlar. Structure of the aramid fibre fabric and required finish determine the appropriate application.

Aramid fabrics

Balanced aramid fabrics (G. ANGELONI s.r.l.)

Reference Areal weight (g/sqm) Weaving style Material / Linear density Thickness (mm)
Warp Weft
Style 120 60 plain aramid 220 dtex aramid 220 dtex 0,07
KK 140 P 140 plain aramid 1210 dtex aramid 1210 dtex 0,18
STYLE 281 170 plain aramid 1210 dtex aramid 1210 dtex 0,22
STYLE 285 170 4H satin aramid 1210 dtex aramid 1210 dtex 0,22
KK 170 T 170 twill 2/2 aramid 1210 dtex aramid 1210 dtex 0,22
KK 170 F 170 fish aramid 1210 dtex aramid 1210 dtex 0,22
STYLE 284 170 plain aramid 1610 dtex aramid 1610 dtex 0,22
KK 220 P/T 220 plain / twill 2/2 aramid 1610 dtex aramid 1610 dtex 0,25
KK 300 P/T/H 300 plain / twill / 5H satin aramid 3320 dtex aramid 3320 dtex 0,35
KK 400 PAN 400 panama aramid 3420 dtex aramid 3420 dtex 0,60
KK 460 P/T 460 plain/twill 2/2 aramid 3420 dtex aramid 3420 dtex 0,60
KK 600 PAN 600 panama aramid 3420 dtex aramid 3420 dtex 127 tex 0,60
This chart contains only a part of the assortment of G. Angeloni s.r.l.. The complete information (catalogue) will be obtained on request.
up

Balanced aramid fabrics (C. Cramer GmbH & Co. KG)

Reference Areal weight (g/sqm) Weaving style Material / Linear density Thickness (mm)
Warp Weft
Style 240 36 plain aramid 22 tex aramid 22 tex 0,10
Style 120 61 plain aramid 22 tex aramid 22 tex 0,12
Style 220 75 plain aramid 42 tex aramid 42 tex 0,15
Style 140 110 twill 2/2 aramid 42 tex aramid 42 tex 0,20
Style 145 115 plain aramid 42 tex aramid 42 tex 0,20
Style 161 120 plain aramid 127 tex aramid 127 tex 0,20
Style 160 158 plain aramid 158 tex aramid 158 tex 0,28
Style 344 160 scrim aramid 158 tex aramid 158 tex 0,50
Style 500 160 plain aramid 158 tex aramid 158 tex 0,30
Style 502 160 twill 2/2 aramid 158 tex aramid 158 tex 0,30
Style 181 170 satin 1/7 aramid 42 tex aramid 42 tex 0,30
Style 281 170 plain aramid 127 tex aramid 127 tex 0,29
Style 284 170 twill 2/2 aramid 127 tex aramid 127 tex 0,30
Style 285 170 satin 3/1 aramid 127 tex aramid 127 tex 0,32
Style 332 195 twill 2/2 aramid 158 tex aramid 158 tex 0,35
Style 335 230 satin 3/1 aramid 158 tex aramid 158 tex 0,45
Style 328 230 plain aramid 158 tex aramid 158 tex 0,35
Style 333 230 twill 2/2 aramid 158 tex aramid 158 tex 0,40
Style 343 230 scrim aramid 158 tex aramid 158 tex 0,60
Style 930 285 plain aramid 158 tex aramid 158 tex 0,47
Style 903 315 satin 1/4 aramid 240 tex aramid 240 tex 0,56
Style 900 335 satin 1/4 aramid 240 tex aramid 240 tex 0,60
Style 1000 365 satin 1/7 aramid 158 tex aramid 158 tex 0,62
Style 1350 470 panama 4/4 aramid 240 tex aramid 240 tex 0,78
Style 1355 470 twill 2/2 aramid 316 tex aramid 316 tex 0,78
Style 1356 470 panama 3/3 aramid 316 tex aramid 316 tex 0,81
up

Balanced aramid fabrics (SGL TECHNOLOGIES GmbH)

Reference Areal weight (g/sqm) Weaving style Material / Linear density Thickness (mm)
Warp Weft
PDL 180 plain aramid 160 tex aramid 160 tex 0,30
up

Unidirectional aramid fibers

Unidirectional aramid fabrics

Reference Areal weight (g/sqm) Weaving style Material / linear density Thickness (mm)
UD AS 200 200 2 scrims aramid 805 tex 0,36
UD AS 300 300 2 scrims aramid 805 tex 0,54
up

Aramid tapes and sleeves

Balanced aramid tapes

Reference Areal weight (g/sqm) Weaving style Material / linear density Thickness (mm)
Warp Weft
KT-B 170 170 plain aramid 1210 dtex aramid 1210 dtex 0,22
KT-B 220 225 plain aramid 1610 dtex aramid 1610 dtex 0,27
KT-U 150 150 plain aramid 2420 dtex aramid 220 tex 0,18
KT-U 200 200 plain aramid 3220 dtex aramid 220 tex 0,23
up

Aramid braided tapes

Reference Areal weight (kg/100 m) Width (mm) stretched / flat Width at 45° (mm) Wall thickness (mm)
Aramid tape 020.26534840-TB  0,625  18 / 22  20  0,25
Aramid tape 025.37443220-TB  1,369  12 / 25  25  0,60
Aramid tape 025.249211610-TB  0,872  17 / 25  25  0,30
Aramid tape 025.249211610-TB, black  0,840  17 / 25  25  0,30
up

Aramid roving

Aramid roving

Reference Linear density Filaments Tensile strength Tensile modulus
1000 840 dtex f 500 2 909 MPa 78 GPa
1000 1100 dtex f1 000 3 046 MPa 78 GPa
1000 1680 dtex f1 000 2 916 MPa 71 GPa
1000 3360 dtex f2 000 2 866 MPa 67 GPa
1014* 1100 dtex f1 000 3 132 MPa 82 GPa
1014* 1680 dtex f1 000 3 082 MPa 74 GPa
1015* 3360 dtex f2 000 2 866 MPa 67 GPa
1040 1680 dtex f1 000 2 916 MPa 70 GPa
1111 420 dtex f 250 2 851 MPa 98 GPa
1055 1610 dtex f1 000 2 929 MPa 110 GPa
1055 3220 dtex f2 000 2 842 MPa 106 GPa
1055 8050 dtex f5 000 2 778 MPa 104 GPa
1056 8050 dtex f5 000 2 778 MPa 104 GPa
2200 1210 dtex f1 000 2 778 MPa 108 GPa
2200 1610 dtex f1 000 3 053 MPa 105 GPa
2200 2420 dtex f2 000 3 067 MPa 105 GPa
2200 3220 dtex f2000 2 923 MPa 105 GPa
2200 4830 dtex f3 000 2 973 MPa 103 GPa
2200 8050 dtex f5 000 2 951 MPa 99 GPa
 
This chart involves a general overview of carbon fibres for information. The availability needs to be checked at specific request.
* Twaron® adhesion activated yarn type.
up

Video

Fotogalerie

Kompozitní materiály jsou laminátové konstrukce ze dvou nebo více složek. Tvrdší, tužší a pevnější výztuž představují tkaniny uhlíkové, aramidové, skelné a jejich hybridy, aluminizované a diolenové tkaniny, rovingy, sendvičové a další materiály. Funkci pojiva zastávají pryskyřice a doplňkové epoxidové systémy.

GRM Systems s.r.o. | Technologická 28 | 779 00 Olomouc | Česká republika
Tel.: +420 585 431 734 | Fax: +420 585 431 994 | email: info@grm-systems.cz | © 2017 GRM
Společnost GRM Systems s.r.o. (hlavní žadatel) a společnost Foller s.r.o. (partner projektu zapojený do realizace) společně realizují projekt Moderní kompozitní matrice (CZ.01.1.02/0.0/0.0/15_019/0005093), jehož cílem je vývoj kompozitních systémů s výrazným zlepšením odolnosti kompozitních profilů na bázi nejmodernějších reaktoplastických systémů matric. Na tento projekt je poskytována finanční podpora od Evropské unie (OPPIK).